| High-Performance Haynes Alloy Pipe — Specification Overview | |||||||||||
| Grade | UNS No. | Base Metal | Strengthening Mechanism | Nominal Composition (wt%) | Max Oxidation-Resistance Temp (°C) | Long-Term Service Temp (°C) | Tensile Strength (MPa) | Yield Strength 0.2% (MPa) | Elongation (%) | Typical Applications | Pipe/Tube Standard |
| Haynes 214 | N07214 | Nickel-base | Solid-solution (with γ′) | Ni bal., Cr 16, Al 4.5, Fe 3, Y 0.01 | 1260 | ≤925 | 830 | 390 | 35 | Furnace components, thermocouple protection tubes, chemical pyrolysis furnace tubes | ASTM B622/B619/B626 |
| Haynes 230 | N06230 | Nickel-base | Solid-solution | Ni bal., Cr 22, W 14, Mo 2, Co 5 max, Al 0.3, C 0.1, La 0.03 | 1149 | 650–980 | 820 | 390 | 45 | Gas turbines, industrial furnace tubes, nitric acid catalyst grids, waste-incineration equipment | ASTM B622/B619/B626 |
| Haynes 242 | N10242 | Nickel-base | Age-hardenable (γ″) | Ni bal., Mo 25, Cr 8, Fe 2 | 816 | 649–704 | 1380 | 1100 | 40 | Gas turbine seals, low-expansion high-temperature components | By agreement (mostly sheet) |
| Haynes 25 (L-605) | R30605 | Cobalt-base | Solid-solution | Co bal., Cr 20, W 15, Ni 10, Mn 1.5, C 0.1 | 1095 | 650–980 | 1000 | 450 | 40 | Aero-engine combustors, turbine components, heat-treatment furnaces | ASTM B622 (pipe by agreement) |
| Haynes 188 | R30188 | Cobalt-base | Solid-solution | Co bal., Ni 22, Cr 22, W 14, Fe 3 max, La 0.03 | 1095 | 650–1095 | 950 | 480 | 50 | Gas turbine combustors, flame tubes, heat exchangers | ASTM B622/B619 |
| Haynes 556 | R30556 | Iron-base | Solid-solution | Fe bal., Ni 20, Co 18, Cr 22, Mo 3, W 2.5, Ta 0.6 | 1095 | ≤1095 | 750 | 380 | 45 | Pulp & paper, heat treatment, petrochemical pyrolysis furnace tubes | ASTM B622/B619/B626 |
| Haynes 625 | N06625 | Nickel-base | Solid-solution | Ni bal., Cr 21.5, Mo 9, Nb 3.6, Fe 5 max | 980 | ≤980 | 830 | 420 | 45 | Chemical, marine, aerospace, oil & gas pipelines | ASTM B444/B704/B705 |
| Haynes 718 | N07718 | Nickel-base | Age-hardenable (γ″) | Ni 52, Fe 19, Cr 18, Nb+Ta 5, Mo 3, Ti 0.9, Al 0.5 | 650 | ≤650 | 1275 | 1035 | 20 | Aerospace, fasteners, petrochemical high-temperature parts | Pipe uncommon; mostly bar/forgings (B637) |
| Haynes 282 | N07208 | Nickel-base | Age-hardenable (γ′) | Ni bal., Cr 20, Co 10, Mo 8.5, Ti 2.1, Al 1.5 | 871 | ≤871 | 1180 | 810 | 25 | Aero-engine turbine discs, gas turbine high-temperature components | Mostly forgings/bar |
Taizhou Hosea Special Alloy Co., Ltd.
البريد الإلكتروني : 17502307545@163.com
ADD. :
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
Fill in more information so that we can get in touch with you faster
Privacy statement: Your privacy is very important to Us. Our company promises not to disclose your personal information to any external company with out your explicit permission.
الآن الاتصال